Труды КНЦ вып.9 (ХИМИЯ И МАТЕРИАЛОВЕДЕНИЕ вып. 1/2018(9) Часть 2)

Kalinkina Elena Vladimirovna PhD (Engineering), I. V. Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials of the Federal Research Centre “Kola Science Centre of the Russian Academy of Sciences”, Apatity, Russia kalinkina@chemy.kolasc.net.ru Tyukavkina Vera Vladimirovna PhD (Engineering), I. V. Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials of the Federal Research Centre “Kola Science Centre of the Russian Academy of Sciences”, Apatity, Russia tukav_vv@chemy.kolasc.net.ru DOI: 10.25702/KSC.2307-5252.2018.9.1.832-837 УДК 666.9 : 53.091 ВЛИЯНИЕ АТМОСФЕРЫ МЕХАНОАКТИВАЦИИ ШЛАКОВ ЦВЕТНОЙ МЕТАЛЛУРГИИ НА ИХ ГИДРАТАЦИЮ А. М. Калинкин1, Санжай Кумар2, Б. И. Гуревич1, Т. К. Алекс2, Е. В. Калинкина1, С. К. Нат2, В. В. Тюкавкина1, Ракеш Кумар2 1Институт химии и технологии редких элементов и минерального сырья им. И. В. Тананаева ФИЦ КНЦ РАН, г. Апатиты, Россия 2Национальная металлургическая лаборатория, г. Джамшедпур, Индия Аннотация Представлены результаты исследований, направленных на повышение реакционной способности гранулированного Cu-Ni-шлака комбината «Печенганикель» и Zn-шлака предприятия “Hindustan Zinc Ltd.” с целью получения на их основе геополимеров и других вяжущих веществ. С применением данных изотермической калориметрии показано, что механоактивация шлаков в атмосфере СО 2 заметно повышает скорость их гидратации по сравнению с механоактивацией в воздушной среде. Механоактивация шлаков в углекислом газе способствует также росту прочности при сжатии цементного камня. Ключевые слова: шлаки цветной металлургии, гидратация, механоактивация, углекислый газ, калориметрия. INFLUENCE OF ATMOSPHERE OF MECHANICAL ACTIVATION OF NON-FERROUS METALLURGY SLAGS ON THEIR HYDRATION A. M. Kalinkin1, Sanjay Kumar2, B. I. Gurevich1, T. C. Alex2, E. V. Kalinkina1, S. K. Nath2, V. V. Tyukavkina1, Rakesh Kumar2 11. V. Tananaev Institute of Chemistry and Technology of Rare Elements and Mineral Raw Materials of the Federal Research Centre “Kola Science Centre of the Russian Academy of Sciences”, Apatity, Russia 2National Metallurgical Laboratory, Jamshedpur, India Abstract Results of investigation towards increasing the reactivity of granulated Cu-Ni slag from “Pechenganickel” smelter plant and Zn slag from M/s Hindustan Zinc Ltd. in order to prepare geopolymers and other binding materials on their basis have been presented. With the use of isothermal calorimetry data it has been shown that mechanical activation of the slags in CO 2 atmosphere notably increases the rate of their hydration in comparison to mechanical activation in air. Mechanical activation of the slags in carbon dioxide promotes also the development of compressive strength of the cement stone. Keywords : non-ferrous metallurgy slags, hydration, mechanical activation, carbon dioxide, calorimetry. Ежегодно в мире в качестве отходов переработки различных руд производится огромное количество металлургических шлаков, исчисляемое сотнями миллионов тонн [1]. Наиболее рациональным способом утилизации шлаков является получение композиционных вяжущих на основе традиционного портландцемента, а также применение в составе относительно новых видов цементов, таких как вяжущие щелочной активации [2, 3]. Вяжущие щелочной активации или геополимеры - перспективный класс материалов, которые получают в результате взаимодействия природных и синтетических силикатов и алюмосиликатов со щелочными агентами. Их отличают высокие физико­ механические характеристики, а также сравнительная простота процесса получения, при котором существенно снижены выбросы СО 2 в окружающую среду. Вяжущие щелочной активации могут применяться не только в строительстве, но и 832