Труды КНЦ вып.5 (ХИМИЯ И МАТЕРИАЛОВЕДЕНИЕ вып. 5/2015(31))

Петрозаводский государственный университет, г.Петрозаводск, Россия, shulga.alisa@gmail.com Ханина Елена Яковлевна, к.х.н., Петрозаводский государственный университет, Петрозаводск, Россия, ohanina@sampo.ru Stepanova Kristina Vyacheslavovna, Petrozavodsk State University, Petrozavodsk, Russia , lady.cristin4ik@yandex.ru Iakovleva Natalia Mikhailovna, Dr. Sc. (Physics and Mathematics), Petrozavodsk State University, Petrozavodsk, Russia, nmyakov@gmail.com Kokatev Aleksandr Nikolaevich, PhD (Engineering), Petrozavodsk State University, Petrozavodsk, Russia , nelan-oksid@bk.ru Shulga Alisa Mihailovna, Petrozavodsk State University, Petrozavodsk, Russia, shulga.alisa@gmail.com Khanina Elena Iakovlevna, PhD (Chemistry), Petrozavodsk State University, Petrozavodsk, Russia, ohanina@sampo.ru УДК666.762 СВОЙСТВА ВЫСОКОТЕМПЕРАТУРНЫХ КЕРАМИЧЕСКИХ ПОКРЫТИЙ НА ОСНОВЕ МУЛЛИТА С.С. Стрельникова, Н.Т. Андрианов, А.С. Анохин Институт металлургии и материаловедения им. А.АБайкова РАН, Москва, Россия Аннотация Работа посвящена разработке термостойких защитных покрытий на карбидкремниевые нагреватели. Синтезированные покрытия состоят из тонкодисперсного муллита, полученного золь-гель методом, и зернистого SiC. Использовали один из вариантов золь-гель метода, что позволило получить высокодисперсные, активные к спеканию порошки муллита на основе водных растворов неорганических солей алюминия и кремнеземсодержащего компонента («белой сажи» - БС) с поливиниловым спиртом в качестве гелеобразователя. Проанализировано влияние температуры синтеза муллита и температуры вжигания покрытия на его свойства. Установлена зависимость количества карбида кремния на свойства материала. Изучены свойства и поведение высокотемпературных защитных покрытий после термоциклирования. Ключевые слова : муллитовая керамика (3AhOr2SiO2), золь-гель метод, муллитовые золь-гель порошки, высокотемпературные защитные покрытия. PROPERTIES OF HIGH-TEMPERATURE CERAMICS COATINGS BASED ON MULLITE S.S. Strelnikova, N.T. Andrianov, A.S. Anokhin A.A.Baikov Institute o f Metallurgy and Material Science o f the RAS, Moscow, Russia Abstract The work is dedicated to development of thermostable protective coatings on SiC substrates. They consist of granular SiC and fine mullite powder (3Al2O3*2SiO2) prepared by sol-gel techniques. In recent times to receive active in sintering powder commonly used chemical methods, including sol-gel technology. Using sol-gel method we have produced fine, active for sintered powder mullite from aqueous solutions of inorganic salts of aluminium and tecknical product ("white carbon black" - BS) fine SiO 2 , applying a polyvinylalcohol. The effect of temperature of synthesis of a mullite and of temperature of heating of coatings was studied. The influence of quantity of SiC on properties of material was established. The work was to study properties of high-temperature protective coatings after thermocycling. Keywords: mullite ceramics (3AhO3,2SiO2), sol-gel technology, mullite sol-gel powders, thermostable protective coatings. Эксплуатационная надежность конструкционных материалов на основе неоксидных соединений (карбида и нитрида кремния, углерода и др.) в значительной степени может быть повышена за счет создания функциональных покрытий, защищающих поверхность эксплуатируемого материала от воздействия различных агрессивных факторов, в первую очередь, от высокотемпературного окисления. Особое место в технике высоких температур занимает карбид кремния (SiC) и керамика на его основе, в частности карбидкремниевые нагреватели, температура и продолжительность службы которых существенно зависят от их способности противостоять окислению. Использование композиционных материалов на основе SiC в окислительных условиях ограничивается возможностью окисления углерода при температурах выше 479