Труды КНЦ вып.5 (ХИМИЯ И МАТЕРИАЛОВЕДЕНИЕ вып. 5/2015(31))

Сведения об авторах Кушхов Хасби Билялович, д.х.н., Кабардино-Балкарский государственный университет им. Х.М.Бербекова, г.Нальчик, Россия, hasbikushсhov@yahoo.com Кучмезова Фатимат Юсуповна, Кабардино-Балкарский государственный университет им. Х.М.Бербекова, г.Нальчик, Россия, fatima.kuchmezova. 8 6 @mail.ru Адамокова Марина Нургалиевна, к.х.н., Кабардино-Балкарский государственный университет им. Х.М.Бербекова, г.Нальчик, Россия, adamokovam 1 @yahoo .com Kushkhov Khasbi Bilyalovich, Dr.Sc. (Chemistry), Kh.M.Berbekov Kabardino-Balkarian State University, Nalchik, Russia , hasbikushсhov@yahoo.com Кuchmezova Fatimat Yusupovna, Kh.M.Berbekov Kabardino-Balkarian State University, Nalchik, Russia , fatima.kuchmezova. 8 6 @mail.ru Adamokova Marina Nurgalievna, PhD (Chemistry), Kh.M.Berbekov Kabardino-Balkaria State University, Nalchik, Russia , adamokovam1@yahoo.com УДК 621.357:546.883 СИНТЕЗ КОМПОЗИЦИОННОГО МАТЕРИАЛА НИТИНОЛ-ТАНТАЛ В СОЛЕВЫХ РАСПЛАВАХ Е.А. Маренкова, С.А. Кузнецов Институт химии и технологии редких элементов и минерального сырья им. И.В.Тананаева Кольского научного центра РАН, Апатиты, Россия Аннотация Исследовано электровосстановление комплексов тантала в хлоридно-фторидном расплаве на электродах из меди, вольфрама и нитинола. С использованием стационарного и импульсного режимов электролиза в расплаве NaCl-KCl- NaF (10 мас. %)-K2TaF7 (10 мас. %) при температуре 1023 Kполучены покрытия тантала на подложке из нитинола. Измерена шероховатость полученных покрытий, адгезия покрытий тантала к подложке, определена пористость покрытий тантала методом Эрхардта и коррозионная стойкость композиции нитинол-тантал в разбавленных растворах минеральных кислот и в солевом растворе хлорида натрия. Ключевые слова: композиционные материалы, хлоридно-фторидные расплавы, нитинол, тантал, защитные покрытия. SYNTESIS OF THE NITINOL-TANTALUM COMPOSITION MATERIAL IN MOLTEN SALTS E.A. Marenkova, S.A. Kuznetsov I. V. Tananaev Institute of Chemistry and Technology o f Rare Elements and Mineral Raw Materials, Kola Science Centre o f the RAS, Apatity, Russia Abstract Electroreduction of the tantalum complexes in chloride-fluoride melt on the copper, tungsten and nitinol electrodes, was investigated. The tantalum coatings on the nitinol substrate in the NaCl-KCl-NaF(10 wt.%)-K2TaF7(10 wt.%) melt at the temperature of 1023 K, were obtained using stationary and pulsed electrolysis. The roughness of the coatings was measured, the tantalum coatings adhesion to the substrate was defined, the porosity of the tantalum coatings was measured by Ehrhardt's technique and the corrosion resistance of the tantalum-nitinol composition in dilute mineral acids and sodium chloride solution, was determined. Keywords: composition materials, chloride-fluoride melts, nitinol, tantalum, protective coatings. Введение Никель-титановые сплавы (нитинол) широко используются как биоматериалы для медицинских имплантатов вследствие их уникальных свойств, таких как эффект запоминания формы, эластичность и др. Однако с течением времени вследствие коррозии в организм попадают опасные для здоровья ионы никеля, обладающие аллергическим, токсическим и канцерогенным действием [1]. В свою очередь, тантал обладает исключительной коррозионной стойкостью и совершенно не раздражает живую ткань [2, 3]. Но из-за высокого удельного веса тантала целесообразнее использовать не компактный металл, а его покрытия на различных подложках. Таким образом, актуальной задачей является улучшение коррозионной стойкости нитинола, что может быть достигнуто за счет нанесения защитных покрытий из тантала. 256